weicon zinc spray 亮锌喷剂400 ml (bright grade)
weicon zinc spray provides all metal surfaces, such as hot-dip
galvanised parts being repaired, with permanent, cathodic corrosive
protection. it forms a quick-drying, adhesive, protective layer of
microfine zinc flakes.
in a salt spraying test according to din 53167 or din 50021, metal
parts sprayed with weicon zinc spray showed no corrosion, even after
more than 550 hours. the innovative zinc flakes form a highly resistant
protective layer, even against extreme weather and environmental
influences. in this way, weicon zinc spray fulfils higher requirements
than demanded in din en iso 1461. the colour of weicon zinc spray
"bright grade" has been adapted to that of hot-dip galvanisation.
applications
• as high-quality rust protection primer
• for touching up welded or drilled sections
• as a conductive intermediate layer in spot welding
• wherever metal must be protected from corrosion
purchase data
item number 11001400
gtin 4024596000387
item features
colour ral 9006, "fresh hot-dip galvanisation" 
application indoors and outdoors 
binding agent modified alkyd resin 
pigment flaky zinc and aluminium pigments 
pigment purity about 99,9 zn / approx. 99,5 al 
percentage of metal in dry film ca. 70 %
content 400 ml
specific weight 1,0 - 1,2 g/cm³
recommended primer zinc spray 
processing temperature +5 to +35, optimum temperature from +18 to + 25 °c
consumption at 1.5 cross coats ca. 150 ml/m²
layer thickness at 1.5 cross coats ca. 20-40 µm
dust dry after ca. 15 min.
hardened after ca. 12 h
paintable ca. 24 h
abrasion-resistant abrasion-resistant 
cross cutting din 53151 / iso 2409 cross cut characteristic value gt 0 to gt 1 
salt spraying test iso 9227 >240 h
mandrel bend test din en iso 1519 no hair cracking 
top coating not required 
temperature resistance after complete hardening about -50 to +300 °c
storage stability 24 months

---