lexan? homopolymer
hp1
region americas
description
high flow polycarbonate. for medical devices and pharmaceutical applications. healthcare management of change,
biocompatible (iso10993 or usp class vi). eto sterilizable. contains mold release.
typical property values
properties typical values units test methods
mechanical
tensile stress, yld, type i, 50 mm/min 62 mpa astm d 638
tensile stress, brk, type i, 50 mm/min 65 mpa astm d 638
tensile strain, yld, type i, 50 mm/min 6 % astm d 638
tensile strain, brk, type i, 50 mm/min 120 % astm d 638
tensile modulus, 50 mm/min 2370 mpa astm d 638
flexural stress, yld, 1.3 mm/min, 50 mm span 93 mpa astm d 790
flexural modulus, 1.3 mm/min, 50 mm span 2300 mpa astm d 790
hardness, rockwell m 70 - astm d 785
hardness, rockwell r 118 - astm d 785
taber abrasion, cs-17, 1 kg 10 mg/1000cy astm d 1044
tensile stress, yield, 50 mm/min 63 mpa iso 527
tensile stress, break, 50 mm/min 50 mpa iso 527
tensile strain, yield, 50 mm/min 6 % iso 527
tensile strain, break, 50 mm/min 70 % iso 527
tensile modulus, 1 mm/min 2350 mpa iso 527
flexural stress, yield, 2 mm/min 90 mpa iso 178
flexural modulus, 2 mm/min 2300 mpa iso 178
impact
izod impact, unnotched, 23°c 3204 j/m astm d 4812
izod impact, notched, 23°c 640 j/m astm d 256
izod impact, notched (natural, tints) 640 j/m astm d 256
tensile impact, type s 378 kj/m? astm d 1822
falling dart impact (d 3029), 23°c 169 j astm d 3029
instrumented impact energy @ peak, 23°c 54 j astm d 3763
? 2017 copyright by sabic. all rights reserved
izod impact, unnotched 80*10*4 +23°c na kj/m? iso 180/1u
izod impact, unnotched 80*10*4 -30°c na kj/m? iso 180/1u
izod impact, notched 80*10*4 +23°c 12 kj/m? iso 180/1a
izod impact, notched 80*10*4 -30°c 10 kj/m? iso 180/1a
charpy 23°c, v-notch edgew 80*10*4 sp=62mm 12 kj/m? iso 179/1ea
charpy -30°c, v-notch edgew 80*10*4 sp=62mm 10 kj/m? iso 179/1ea
thermal
hdt, 1.82 mpa, 3.2mm, unannealed 126 °c astm d 648
hdt, 0.45 mpa, 6.4 mm, unannealed 137 °c astm d 648
hdt, 1.82 mpa, 6.4 mm, unannealed 126 °c astm d 648
cte, -40°c to 95°c, flow 6.84e-05 1/°c astm e 831
specific heat 1.25 j/g-°c astm c 351
thermal conductivity 0.19 w/m-°c astm c177
thermal conductivity 0.2 w/m-°c iso 8302
cte, 23°c to 80°c, flow 7.e-05 1/°c iso 11359-2
ball pressure test, 125°c +/- 2°c passes - iec 60695-10-2
vicat softening temp, rate b/50 139 °c iso 306
vicat softening temp, rate b/120 140 °c iso 306
hdt/be, 0.45mpa edgew 120*10*4 sp=100mm 133 °c iso 75/be
hdt/ae, 1.8 mpa edgew 120*10*4 sp=100mm 121 °c iso 75/ae
relative temp index, elec 130 °c ul 746b
relative temp index, mech w/impact 130 °c ul 746b
relative temp index, mech w/o impact 130 °c ul 746b
physical
specific gravity 1.2 - astm d 792
specific volume 0.83 cm?/g astm d 792
density 1.19 g/cm? astm d 792
water absorption, 24 hours 0.15 % astm d 570
water absorption, equilibrium, 23c 0.35 % astm d 570
water absorption, equilibrium, 100°c 0.58 % astm d 570
mold shrinkage, flow, 3.2 mm (5) 0.5 – 0.7 % sabic method
melt flow rate, 300°c/1.2 kgf 25 g/10 min astm d 1238
melt volume rate, mvr at 300°c/1.2 kg 23 cm?/10 min iso 1133
optical
light transmission, 2.54 mm 88 % astm d 1003
haze, 2.54 mm 1 % astm d 1003
refractive index 1.586 - astm d542
electrical
properties typical values units test methods
? 2017 copyright by sabic. all rights reserved
volume resistivity >1.e+17 ohm-cm astm d 257
dielectric strength, in air, 3.2 mm 14.9 kv/mm astm d 149
relative permittivity, 50/60 hz 3.17 - astm d 150
relative permittivity, 1 mhz 2.96 - astm d 150
dissipation factor, 50/60 hz 0.0009 - astm d 150
dissipation factor, 1 mhz 0.01 - astm d 150
hot wire ignition {plc) 2 plc code ul 746a
high voltage arc track rate {plc} 2 plc code ul 746a
high ampere arc ign, surface {plc} 1 plc code ul 746a
comparative tracking index (ul) {plc} 2 plc code ul 746a
volume resistivity >1.e+15 ohm-cm iec 60093
surface resistivity, roa >1.e+15 ohm iec 60093
dielectric strength, in oil, 3.2 mm 17 kv/mm iec 60243-1
relative permittivity, 1 mhz 2.7 - iec 60250
dissipation factor, 50/60 hz 0.001 - iec 60250
dissipation factor, 1 mhz 0.01 - iec 60250
relative permittivity, 50/60 hz 2.7 - iec 60250
flame characteristics
ul recognized, 94v-2 flame class rating (3) 1.09 mm ul 94
oxygen index (loi) 25 % iso 4589
injection molding
drying temperature 120 °c
drying time 3 – 4 hrs
drying time (cumulative) 48 hrs
maximum moisture content 0.02 %
melt temperature 270 – 295 °c
nozzle temperature 265 – 290 °c
front - zone 3 temperature 270 – 295 °c
middle - zone 2 temperature 260 – 280 °c
rear - zone 1 temperature 250 – 270 °c
mold temperature 70 – 95 °c
back pressure 0.3 – 0.7 mpa
screw speed 40 – 70 rpm
shot to cylinder size 40 – 60 %
vent depth 0.025 – 0.076 mm
properties typical values units test methods
? 2017 copyright by sabic. all rights reserved
description
tbd
disclaimer
any sale by sabic, its subsidiaries and affiliates (each a “seller”), is made exclusively under seller’s standard conditions of sale
(available upon request) unless agreed otherwise in writing and signed on behalf of the seller. while the information contained herein
is given in good faith, seller makes no warranty, express or implied, including merchantability and
noninfringement of intellectual property, nor assumes any liability, direct or indirect, with respect
to the performance, suitability or fitness for intended use or purpose of these products in any
application. each customer must determine the suitability of seller materials for the customer’s particular use through appropriate
testing and analysis. no statement by seller concerning a possible use of any product, service or design is intended, or should be
construed, to grant any license under any patent or other intellectual property right.
东莞市宇峰塑胶化工有限公司
唐先生
18929121615
广东 东莞 樟木头镇 樟木头塑胶商务中心5栋76号