tritan™ ex401
共聚多酯
产品说明:
tritan™ ex401, specifically developed for the infant care market, is an amorphous copolyester with excellent appearance and clarity. tritan™ ex401 contains a mold release derived from vegetable based sources. its most outstanding features are clarity, excellent toughness, hydrolytic stability, and heat and chemical resistance. tritan™ ex401 meets infant care sterilization requirements via boiling water or microwave steam sterilization. this new-generation copolyester can also be molded into various applications without incorporating high levels of residual stress. combined with tritan™ copolyester's outstanding chemical resistance and hydrolytic stability, these features give molded products enhanced durability in the dishwasher environment, which can expose products to high heat, humidity, and aggressive cleaning agents.
tritan™ ex401 can be converted into parts using injection molding, injection stretch blow molding (isbm), and extrusion blow molding techniques.
tritan™ ex401 copolyester may be used in repeated use food contact articles under united states food and drug administration (fda) regulations. contact eastman representative for details on global food contact regulatory clearances.
eastman tritan™ ex401 copolyester is included in eastman chemical company's customer notification procedure which details our policy for customer notification when significant changes are made in tritan™ ex401 sold into the infant care market. this procedure provides the infant care industry an added layer of confidence in the consistent quality and performance of tritan.
单位: 公制 | 英制
总体
材料状态
已商用：当前有效
资料 1
ul 黄卡 2
搜索 ul 黄卡
eastman chemical company tritan™
供货地区
北美洲非洲和中东 拉丁美洲欧洲 亚太地区
添加剂
脱模
特性
共聚物抗撞击性，高可加工性，良好耐化学性良好耐热性，高 清晰度，高韧性良好食品接触的合规性水解稳定脱模性能良好 外观良好无定形的用蒸汽消毒
用途
infant care 瓶子 橡皮奶头
机构评级
fda 食品接触, 未评级
加工方法
injection stretch blow molding 挤出吹塑成型 注射成型
物理性能 额定值
单位制
测试方法
比重
1.17
astm d792
收缩率 - 流动
blow molded
0.012 到 0.016
in/in
内部方法
注塑
5.0e-3 到 7.0e-3
in/in
astm d955
硬度 额定值
单位制
测试方法
洛氏硬度 (r 级, 73°f)
115
astm d785
机械性能 额定值
单位制
测试方法
拉伸模量
73°f
230000
psi
astm d638
73°f
236000
psi
iso 527-2
抗张强度
屈服, 73°f
6380
psi
astm d638, 内部方法
屈服, 73°f
6530
psi
iso 527-2, 内部方法
断裂, 73°f
7690
psi
astm d638
断裂, 73°f
7110
psi
iso 527-2
伸长率
屈服, 73°f
7.0
%
astm d638, 内部方法, iso 527-2
屈服, 73°f 3
6.5
%
内部方法
断裂, 73°f
140
%
astm d638
断裂, 73°f
130
%
iso 527-2
弯曲模量
73°f
230000
psi
astm d790
73°f
222000
psi
iso 178
弯曲强度 (屈服, 73°f)
9570
psi
astm d790
冲击性能 额定值
单位制
测试方法
悬壁梁缺口冲击强度
-40°f
2.4
ft·lb/in
astm d256
73°f
12
ft·lb/in
astm d256, 内部方法
-40°f
6.7
ft·lb/in²
iso 180
73°f
31
ft·lb/in²
iso 180
无缺口悬臂梁冲击
astm d4812
-40°f
无断裂
73°f
无断裂
装有测量仪表的落镖冲击
astm d3763
-40°f, energy at max load
558
in·lb
73°f, energy at max load
522
in·lb
热性能 额定值
单位制
测试方法
载荷下热变形温度
astm d648
66 psi, 未退火
228
°f
264 psi, 未退火
198
°f
光学性能 额定值
单位制
测试方法
透射率 (总计)
92.0
%
astm d1003
雾度
--
< 1.0
%
astm d1003
-- 4
< 1.0
%
内部方法
补充信息 额定值
单位制
测试方法
fill volume shrinkage 5
内部方法
boiling, 1 hr
< 1.0
%
boiling, 2 hr
< 1.5
%
dishwasher
< 1.0
%
microwave boiling - oven power 5
< 2200
watts
内部方法
microwave steam sterilization - total energy 5
< 11200
w-min
内部方法
thermal shock - water immersion 5 (95 到 208°f)
no effect
内部方法
注射 额定值
单位制
干燥温度
190
°f
干燥时间
4.0 到 6.0
hr
加工（熔体）温度
500 到 540
°f
模具温度
100 到 151
°f
注射说明
injection stretch blow molding parameters:
processing melt temperature: 270 to 285°c
injection mold temperature: 60 to 70°c
preform temperature at blow: 185 to 195°c
primary blow pressure: 0.03 to 0.08 mpa
blow mold temperature: 80 to 90°c
residual stress under polarized light, fringe count, emn: <=3
挤出 额定值
单位制
熔体温度
464 到 482
°f
挤压说明
extrusion blow molding mold temperature: 25 to 45°c
备注
1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。
2ul 黄卡含有 ul 验证的易燃性和电气特性。ul prospector 持续努力在 prospector 中将黄卡链接至单个塑料材料，然而此列表可能未包括所有相应链接。重要的是，我们对 prospector 中找到的这些黄卡和塑料材料之间的关联进行验证。如需完整的黄卡列表，请访问 ul 黄卡搜索。
3after re-equilibration
4after 8 hr boiling
5isbm bottle
深圳市华聚塑料原料有限公司
15118304901
中国 东莞